После закалки и отпуска бесшовных труб, производимые детали имеют хорошие комплексные механические свойства и широко используются в различных важных деталях конструкций., особенно те шатуны, болты, шестерни и валы, работающие при переменных нагрузках. Но твердость поверхности низкая и не износостойкая.. Темперирование + surface quenching can be used to improve the surface hardness of parts.
Its chemical composition contains carbon (C) content of 0.42~0.50%, Si content of 0.17~0.37%, Mn content of 0.50~0.80%, and Cr content<=0.25%.
Recommended heat treatment temperature: normalizing 850°C, quenching 840°C, tempering 600°C.
Common seamless steel pipes are generally made of high-quality carbon structural steel, which is not very hard and easy to cut. It is often used in molds to make templates, tips, guide posts, и т.п., but heat treatment is required.
1. After quenching and before tempering, the hardness of the steel is greater than HRC55, which is qualified.
The highest hardness for practical application is HRC55 (high frequency quenching HRC58).
2. Do not use the heat treatment process of carburizing and quenching for steel.
После закалки и отпуска, the parts have good comprehensive mechanical properties and are widely used in various important structural parts, особенно те шатуны, болты, шестерни и валы, работающие при переменных нагрузках. Но твердость поверхности низкая и не износостойкая.. Темперирование + surface quenching can be used to improve the surface hardness of parts.
Carburizing treatment is generally used for heavy-duty parts with wear-resistant surface and impact-resistant core, и его износостойкость выше, чем при закалке и отпуске + закалка поверхности. Содержание углерода на поверхности составляет 0.8-1.2%, а ядро вообще 0.1-0.25% (0.35% используется в особых случаях). После термической обработки, the surface can obtain very high hardness (HRC58–62), and the core has low hardness and impact resistance.